CASTROL Tribol GR 4020 / 460-2 PD
Industrial Greases and Pastes
Tribol GR 4020/460-2 PD is a petroleum and lithium-complex based grease, which was formulated as multi-service lubricant for heavy duty applications of plain and antifriction bearings under medium to high loads.
Its TGOA additives are very effective in protecting the machined surfaces of bearings during the critical ‘running-in’ period. Good bearing surfaces are essential for long bearing life.
Tribol GR 4020/460-2 PD is commonly used as a plant wide lubricant in the automotive industry as well as industries where the preference is for a high performance non-dark grease (formulated without molybdenum-disulfide).
The recommended application temperature of Tribol GR 4020/460-2 PD is between -20 °C (-4 °F) and +150 °C (+302 °F).
Clasifications:
DIN: KP2N-20
ISO: L-XBDHB-2
Consistency grade: NLGI 2
Typical characteristics:
Worked penetration, 60 strokes at 25 °C (77 °F): 265 - 295 (0.1 mm)
Base oil viscosity at 40 °C (104 °F): 460 mm2/sec
Dropping point: 240 °C (464 °F)
Four Ball Weld Load test, Weld Point, ASTM D2596: 400 kgf
Four Ball Wear test - Weld Load, DIN 51350-4: 4200/4400 N
Four Ball Wear test - Wear Scar Diameter, 40 kgf/75°C/1200rpm/1hr: 0.5 mm
SRV Friction and Wear test, 300N/2hr/50°C: 0.08 coeff of friction
Its TGOA additives are very effective in protecting the machined surfaces of bearings during the critical ‘running-in’ period. Good bearing surfaces are essential for long bearing life.
Tribol GR 4020/460-2 PD is commonly used as a plant wide lubricant in the automotive industry as well as industries where the preference is for a high performance non-dark grease (formulated without molybdenum-disulfide).
The recommended application temperature of Tribol GR 4020/460-2 PD is between -20 °C (-4 °F) and +150 °C (+302 °F).
Clasifications:
DIN: KP2N-20
ISO: L-XBDHB-2
Consistency grade: NLGI 2
Typical characteristics:
Worked penetration, 60 strokes at 25 °C (77 °F): 265 - 295 (0.1 mm)
Base oil viscosity at 40 °C (104 °F): 460 mm2/sec
Dropping point: 240 °C (464 °F)
Four Ball Weld Load test, Weld Point, ASTM D2596: 400 kgf
Four Ball Wear test - Weld Load, DIN 51350-4: 4200/4400 N
Four Ball Wear test - Wear Scar Diameter, 40 kgf/75°C/1200rpm/1hr: 0.5 mm
SRV Friction and Wear test, 300N/2hr/50°C: 0.08 coeff of friction